Aegis® PCR-H120MP

1 of 8 products in this brand
Aegis® PCR-H120MP is a nylon 6 extrusion grade homopolymer made from 100% post-consumer recycled (PCR) materials. It is lubricated, nucleated, and has high viscosity, making it suitable for cast or blown film applications. It combines strength, toughness, and thermoforming properties with excellent heat, chemical, and abrasion resistance.
Technical Data Sheet

Ask AdvanSix Questions

Thomas Clark avatarEd Asirvatham avatarJohn Facinelli avatar
  • TypeDocument Name
View All Documents

Enhanced TDS

Identification & Functionality

Chemical Family
Polyamides
Polymer Name
Polyamide 6 (PA 6)
Plastics & Elastomers Functions
Resin
Technologies
Plastics
Product Families
Plastics — Engineering & Specialty Polymers
Polyamides

Features & Benefits

Materials Features
Abrasion Resistant,
Chemical Resistant,
Excellent Strength,
Excellent Toughness,
Good Thermoformability,
Heat Resistance,
High Viscosity

Applications & Uses

Plastics & Elastomers End Uses
Blown Films,
Cast Films,
Film
Plastics & Elastomers Processing Methods
Blown Film Extrusion,
Cast Film Extrusion,
Extrusion,
Film Extrusion

Properties

Thermal Properties
ValueUnitsTest Method / Conditions
Melting Point220°CASTM D-3418
Physico-Chemical Properties
ValueUnitsTest Method / Conditions
Viscosity (flowable apparent viscosity)120-ASTM D-789
Reactivity Value (at 96% sulfuric acid)3.6--
Extractable Contentmax. 0.8%SOP-702-307
Density1.13g/cm³ASTM D-792
Melt Flow Rate (235°C/1.0 kg)1.9g/10 minASTM D-1238
Gas Barrier Properties
ValueUnitsTest Method / Conditions
Oxygen Permeability (at 23°C/0% RH)40.3cc.25μm/m²/dayASTM D-3985
Water Vapor Permeability (at 38°C/100% RH)992g.25μm/m²/dayF-1249
Nitrogen Permeability (at 23°C/80% RH)14.0cc.25μm/m²/dayASTM D-1434
Carbon Dioxide Permeability (at 23°C/100% RH)72.8cc.25μm/m²/dayASTM D-1434
Moisture Properties
ValueUnitsTest Method / Conditions
Moisture Contentmax. 0.08%ASTM D-6869
Moisture Content (in 24 hours)1.6%ASTM D-570
Moisture Content (at 50% RH)2.7%ASTM D-570
Moisture Content (saturation)9.5%ASTM D-570

Regulatory & Compliance

Certifications & Compliance
EC Regulation 2011/10,
FDA 21 CFR 177.1500

Storage & Handling

Processing Guidelines

Material Handling

Aegis® PCR-H120MP is supplied in sealed containers and drying prior to processing is not required. However, higher moisture is the primary cause of processing issues. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level.

Extrusion Guidelines

Melt Viscosity vs. Temperature

Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F).
Two key factors affect the melt viscosity (stiffness or fluidity of the melt):
1. The molecular weight (MW) of the resin: Higher MW resins will have a higher melt viscosity than lower MW resins.
2. Temperature of the melt for any given MW resin: Higher process temperatures will provide a more fluid melt viscosity than lower process temperatures.


Typical Barrel Profile for Cast Films

Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)
 

Typical Barrel Profile for Cast Films

Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)


Screw Parameters

Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1
 

Metering Section Flight Depth

Screw Diameter

Recommended Depth
1" 0.055"
1.5" 0.060"
2" 0.070"
2.5" 0.080"
3.5" 0.100"
4.5" 0.115"
6" 0.135"