Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Typical Properties
Value | Units | Test Method / Conditions | |
Average Thickness Target (at 73°F (22.7°C), 50% RH) | 15 | micron | AdvanSix Method |
Average Thickness Tolerance (at 73°F (22.7°C), 50% RH) | 5 | % | AdvanSix Method |
Basis Weight (at 73°F (22.7°C), 50% RH) | 17.24 | g/sq.m | AdvanSix Method |
Coefficient of Friction Kinetic (Film to Film at 73°F (22.7°C), 50% RH) | 0.5 - 0.9 | — | ASTM D-1894 |
Coefficient of Friction Kinetic (Film to Metal at 73°F (22.7°C), 50% RH) | 0.2 - 0.3 | — | ASTM D-1894 |
Dimensional Stability - MD (Hot air at 320°F(160°C), 5 mins) | max. 3 | % | — |
Dimensional Stability - TD (Hot air at 320°F(160°C), 5 mins) | max. 2.5 | % | — |
Elongation at Break - MD (at 73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
Elongation at Break - TD (at 73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
Haze (at 73°F (22.7°C), 50% RH) | max. 4 | % | ASTM D-1003 |
Oxygen Transmission Rate (at 77°F/0% RH, 25°C/0% RH) | 47 - 62 | cc/m2 /day | ASTM D-3985 |
Secant Modulus - MD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
Secant Modulus - TD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
Surface Tension Treated Side (at 73°F (22.7°C), 50% RH) | min. 56 | dynes/cm | ASTM D-2578 |
Surface Tension Untreated Side (at 73°F (22.7°C), 50% RH) | 48 - 54 | dynes/cm | ASTM D-2578 |
Tensile Strength at Break - MD (at 73°F (22.7°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
Tensile Strength at Break - TD (at 73°F (22.7°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
Water Vapor Transmission Rate (at 100°F/100% RH, 37.7°C/100% RH) | 310 - 357 | gm/m2 /day | ASTM F-1249 |
Yield (at 73°F (22.7°C), 50% RH) | 58.02 | sq.m/kg | AdvanSix Method |