Value | Units | Test Method / Conditions | |
Average Thickness (Target, 73°F (22.7°C), 50% RH) | 25 | microns | AdvanSix Method |
Average Thickness (Tolerance, 73°F (22.7°C), 50% RH) | ± 5 | % | AdvanSix Method |
Basis Weight (at 73°F (22.7°C), 50% RH) | 29.3 | g/sq.m | AdvanSix Method |
Coefficient of Friction - Kinetic (Film to Film, 73°F (22.7°C), 50% RH) | 0.6 - 0.8 | — | ASTM D-1894 |
Coefficient of Friction - Kinetic (Film to Metal, 73°F (22.7°C), 50% RH) | 0.2 - 0.3 | — | ASTM D-1894 |
Dimensional Stability - MD (at 73°F (22.7°C), 50% RH) | max. 3.0 | % | Hot air at 320ºF (160ºC), 5 mins |
Dimensional Stability - TD (at 73°F (22.7°C), 50% RH) | max. 2.5 | % | Hot air at 320ºF (160ºC), 5 mins |
Elongation at Break - MD (73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
Elongation at Break - TD (73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
Modulus Secant MD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
Modulus Secant TD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
Optical Density | min. 2.2 | — | Macbeth |
Oxygen Transmission Rate (at 73ºF (23ºC), 0% RH) | 0.47 - 1.09 | cc/m²/day | ASTM D-3985 |
Surface Tension Non-Metallized Side (at 73°F (22.7°C), 50% RH) | min. 50 | dynes/cm | ASTM D-2578 |
Tear Strength - Graves (at 73°F (22.7°C), 50% RH) | 600 - 1,000 | — | ASTM D-1004 |
Tensile Strength - MD (at 73°F (23°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
Tensile Strength - TD (at 73°F (23°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
Water Vapor Transmission Rate (at 100ºF (37.7ºC), 100% RH) | 2.64 | gm/m²/day | ASTM F-1249 |
Yield (at 73°F (22.7°C), 50% RH) | 34.13 | sq.m/kg | AdvanSix Method |